Adhesion criteria between water-based inorganic zinc coatings and their topcoats for steel
An edition of Adhesion criteria between water-based inorganic zinc coatings and their topcoats for steel (1999)
By J. Peter Ault
Publish Date
1999
Publisher
Federal Highway Administration
Language
eng
Pages
61
Description:
This report presents the results of a test program designed to investigate, in the laboratory, possible causes for failure of water-based inorganic zinc (WBIOZ) coatings. Failures observed in the field have consisted of either topcoat delamination or the appearance of "freckle rusting" in the cured WBIOZ primer. There are many hypotheses regarding the cause of these failures, but no sufficient explanation exists. Furthermore, there are no proven means to ensure that failures do not occur. The general consensus of the literature is that the failures relate to improper cure of the WBIOZ primer. This improper curing is further hypothesized to relate to environmental conditions. The project initially focused on identifying what relationship, if any, existed between environmental conditions and the observed failure modes. Since a definitive relationship did not exist, further testing was conducted to investigate the effects of substrate salt contamination, improper zinc content in the mixed coating, and the effects of rinsing the primer before topcoating. This report presents the more practical results of the study.